SANDAI Two-Part Indoor Coatings show superior levels of durability, flexibility, adhesion, corrosion resistance, and chemical resistance. It offer superior performance against epoxy and urethane coating technology while allowing for ease of installation. It is a low VOC and minimal odor, fast curing, two part polyaspartic aliphatic polyurea sealer/finish coating. The material is applied in a single or multiple coats by brush, roller, or squeegee at varying thicknesses to a variety of substrates.
- Extended working times that greatly improving the consistency and finish of seamless, resinous concrete flooring systems.
- Rapid Cure Properties. Coating dry within 1-2 hours and drive-on within 24 hours.
- Superb Durability. To ensure ultra product performance, no excessive non-reactive additives added.
Superior Resilience that Lasts. Full chemical cure that resist film tightening over time. Film tightening is a common issue for polyaspartics, which can impair adhesion and increase the potential for coating failure.
Color & Gloss Retention. UV durable clear topcoats provide for a rich and long lasting finish that will not fade, amber or peel.
Superior Adhesion to Concrete & Steel. Designed to effectively absorb into the concrete or steel substrate in order to bond within the pores of the material.
Chemical Resistance to a wide range of commercial and industrial chemicals.
All Climate Application. No limitations for minimum cure temperatures. Can be applied in temperatures well below that of standard epoxies and urethanes.
Clear in color. Other color can be achieved in conjunction with a pigment additive.
- Waterproof. 100% waterproof coatings.
1.45 kgs Clear Kits:
Part A: 1 kg
Part B: 0.45 kg
12 months unopened. Store at 4°C-24°C in a covered area (out of the sun). Material should be kept in a cool dry place prior to application.
|Viscosity||1300±168CPS (25℃, 2-Part Mix)|
|Adhesion||Concrete 4.5Mpa Ceramic Tiles 9.7Mpa|
|Coverage (0.1mm dry film)||3m2/kg|